刘斌
,
李瑛
,
王福会
腐蚀科学与防护技术
用电化学阻抗谱(EIS)技术研究了添加不同质量
百分比浓度的纳米锌粉环氧涂层的腐蚀电化学行为，并与环氧清漆(不含颜料)涂层的腐蚀电化学行为进行对比.结果表明，添加不同质量百分比浓度纳米锌粉环氧涂层与环氧清漆涂层具有不同的电化学阻抗谱特征.纳米锌粉的添加量对涂层的防护性能有显著影响，添加不同质量百分比浓度纳米锌粉环氧涂层防腐蚀性能的优劣顺序为：环氧清漆涂层>20mass%>10mass%>2mass%纳米锌环氧涂层.添加纳米锌粉对环氧涂层的防护性能有2方面的影响：一方面使涂层中的微观缺陷大大增多，涂层的防护性能降低；另一方面，由于锌粉的腐蚀产物可将涂层中部分缺陷堵塞，从而对涂层的防护性能有提高作用.由于在所研究的质量百分比浓度范围内(2mass%～20mass%)，前者起了主导作用，所以综合作用的结果是使涂层的防护性能变差.
s.
关键词:
纳米锌粉
,
nano-sized zinc
,
electrochemical behavior
王苹梅柄初雷零
腐蚀科学与防护技术
用热压的方法合成了若干MAX相化合物，包括相（Ti2AlC和Ti2AlN）和312相（Ti3SiC2和Ti3AlC2）;研究了它们在1 mol/L HCl、1 mol/L NaOH和1 mol/L H2SO4中的电化学性质及其结构与其稳定性的关系.结果表明:在所有溶液中,312型MAX相比211相更稳定;Ti3SiC2 和Ti3AlC2几乎在所有溶液里都发生钝化，而Ti2AlC和Ti2AlN在1 mol/L HCl中活跃地溶解，还伴有大量气泡产生；Ti3SiC2比Ti2AlC、Ti2AlN 和Ti3AlC2更稳定.
关键词:
MAX相
,
polarization curves
,
electrochemical behavior
LI Donggui J.P.Simpson R.Schenk Dalian Acid Proof Pump Plant
,
China. Sulzer Bros.Ltd
,
Winterthur
,
Switzerland.
材料科学技术（英）
The effect of heat treatment on the corrosion performance of austenitic-ferritic duplex stain- less steel COR 25 in aqueous solution containing 60%H_3PO_4+4%H_2SO_4+1500 ppm Cl~- at 95℃ was in- vestigated.When the solution temperature was increased from 950℃ to 1230℃,the corrosion resistance increased by two orders of magnitude, as shown by electrochemical measurements,im- mersion tests and direct observation under the scanning electron microscope.The specimens heat treated at solution temperatures of 950℃ and 1030℃ were severely corroded along the phase boundaries;specimens treated at 113C℃ and 1230℃ tended to selective corrosion caused by the dissimilar chromium contents of the aus- tenite and ferrite phases after heat treatment.
关键词:
heat treatment
,
null
,
null
,
null
叶丽清
,
闫莉莉
,
向明武
,
高云涛
,
贝玉祥
贵金属
采用循环伏安法(CV)和差分脉冲伏安法(DPV)，研究了甲啶铂在多壁碳纳米管-离子液体怱饰玻碳电极(MWNTs-[ODMIM]PF6/GCE)上的电化学行为，建立了甲啶铂的测定方法；以紫外-可见光谱法和电化学方法相结合，研究了甲啶铂与 DNA 的嵌插结合作用。结果表明：甲啶铂在MWNTs-[ODMIM]PF6/GCE上有一对氧化还原峰，氧化峰电位Epa与还原峰电位Epc分别为-0.07 V、-0.36 V，峰电位之差为?E=0.29 V，Ipa/Ipc=1.11。在优化条件下，甲啶铂的氧化峰电流与其浓度在2.66~532μmol/L范围内成良好的线性关系(r=0.9994)，检出限为1.33μmol/L。方法操作简便，准确可靠、灵敏度高，可用于甲啶铂含量的直接测定。
关键词:
分析化学
,
甲啶铂
,
多壁碳纳米管
,
离子液体
,
玻碳电极
,
电化学行为
,
伏安法
FANG Zhaoheng CHEN Jiayong Institute of Chemical Metallurgy
,
Academia Sinica
,
Beijing
,
China CHEN Jiayong Institute of Chemical Metallurgy
,
Academia Sinica
,
Zhongguancun
,
Beijing
,
China
金属学报(英文版)
The anodic behavior of synthetic nickel sulfides in sulfuric acid solutions was studied.When the anodes of Ni_3S_2 ,Ni_7S_6 and NiS are actively dissolved respectively,a solid layer forms on the electrode surface with its nature and composition depending on the potentials applied. Based on the electrochemical phenomena,phase and elemental compositions of the solid layer formed on the electrode surface were determined.The apparent number of electrons transfer- red during dissolution of Ni~(2+)was also measured.It can be considered that there are three parallel reactions ocurred on the electrode:the reaction with formation of HSO_4~- or SO_4~(2-), the reaction with formation of sulfides as intermediates and the reaction of Jorming elemental sulfur.With NiS_2 as an anode,formation of SO_4~(2-)or HSO_4~- can be considered as the only re- action occurred on the electrode.
关键词:
nickel sulfide
,
null
,
null
戴长松
,
张生
,
王殿龙
,
高丽霞
,
胡信国
稀有金属材料与工程
以泡沫铅作为负极集流体制备了卷绕VRLA电池.采用计时电流法、循环伏安曲线、电化学阻抗谱和充放电实验研究了泡沫铅负极的电化学行为,结果表明:泡沫铅负极的真实表面积比铅箔负极的大,因此泡沫铅负极具有较低的过电势,并且不论是在怎样的放电状态下,泡沫铅负极的电化学反应电阻较小;与铅箔负极相比,在10、5和2小时率放电状态下,泡沫铅负极的质量比容量分别增加25.9%,30.0%和48.2%.此外,SEM观察显示,泡沫铅负极表面活性物质为更加细小的晶体颗粒和具有更高的孔率.
关键词:
卷绕铅酸电池
,
泡沫铅负极
,
铅箔负极
,
电化学行为
冉先喆
,
程昊
,
王华明
,
汤海波
,
张凌云
材料热处理学报
采用动电位极化曲线、交流阻抗谱方法研究了激光熔化沉积AerMetl00耐蚀超高强度钢在质量分数为3．5％NaCl溶液中的腐蚀电化学行为，采用点蚀失重法研究了热处理对其在酸性FeCl；溶液中点蚀行为的影响。结果表明：激光沉积态AerMetl00钢具有较强定向生长特征的细小快速凝固树枝晶组织和优良的耐蚀性，但由于在枝晶尺寸范围的凝固偏析，耐蚀性略低于锻件且纵向电化学耐蚀性能低于横向；经热处理之后，耐蚀性明显改善，耐蚀性能优于锻件且横向电化学耐蚀性略低于纵向。激光沉积态由于耐蚀性元素Cr、Mo、Ni在枝晶间的偏析使得枝晶内组织易发生选择性点蚀，层间热影响区二次枝晶形貌的部分消除使得该区与周围区域形成“区域腐蚀电池”进一步加速了点蚀的发展，抗点蚀性较差，热处理后，其点蚀失重速率降低且与锻件相当。
关键词:
激光熔化沉积
,
超高强度钢
,
电化学行为
,
点蚀
王钲源
,
张红艳
,
潘飞
,
黄惠
,
郭忠诚
,
赖耀斌
材料科学与工程学报
doi:10.14136/j.cnki.issn.1673-2812.2015.04.019
采用原位聚合法分别制备聚苯胺/二氧化铈(PANI/CeO2)、聚苯胺/碳化钨(PANI/WC)、聚苯胺/二氧化铈/碳化钨(PANI/CeO2/WC)复合材料,通过X射线粉末衍射(XRD)、傅立叶红外光谱仪(FTIR)和拉曼光谱(Raman)对三种复合材料进行物相和结构分析,并且通过交流阻抗和阳极极化测试材料在65g/L Zn2+150g/L H2SO4体系中的电化学行为.通过实验数据分析,得到了一些具有一定学术意义与应用价值的结果.
关键词:
聚苯胺
,
二氧化铈
,
碳化钨
,
复合材料
,
电化学行为